| Nominal Capacitance | 1 uF | |
| Capacitance Tolerance | ±20 % | |
| DC Rated Voltage | DC 4 V | |
| Rated Current (DC) | 2A | |
| DC Resistance | 30mΩmax. | Measured with 100mA max. |
| Insulation Resistance | 500MΩmin. | |
| Operating Temperature Range | -55 to 85 °C | |
| Storage Temperature Range | -55 to 85 °C | |
| Dimensions (L x W x T) | 1.0±0.05 x 0.5±0.1 x 0.3±0.05 mm | Using calipers |
| Capacitance Measurement Frequency | 1.0±0.1kHz | |
| Capacitance Measurement Voltage | 0.5V±0.1V(rms) for [NFM15PC474/105/435] | |
| Withstanding Voltage Test | Rated Voltage x 300% for 1 to 5 s | |
| Solderability | Electrodes shall be at least 90% covered with new solder coating. | Ethanol solution of rosin, 25(wt)%, Pre-heat: 150±10°C, 60 to 90s, Solder: Sn-3.0Ag-0.5Cu, Solder Temperature: 240 ± 3°C, Immersion Time: 3±1 s |
| Resistance to soldering heat | Appearance No damaged, Cap. Change Within ±7.5%, DC Resistance 0.05Ωmax. | Ethanol solution of rosin, 25(wt)%, Pre-heat: 150±10°C, 60 to 90s, Solder: Sn-3.0Ag-0.5Cu, Solder Temperature: 270 ± 5°C, Immersion Time: 10 ± 1 s |
| Bending Strength | Deflection 1.0 mm | Soldered on glass-epoxy substrate (100×40×0.8mm) |
| Drop Test | Height 1m | Dropped on concrete or steel board, Free fall, 3 directions |
| Bonding Strength | Applying Force (F): 5 N | Soldered on glass-epoxy substrate, Applying Time: 10 s |
| Vibration Test | Total amplitude 3.0 mm or Acceleration amplitude 196m/s² whichever is smaller. | Soldered on glass-epoxy substrate, Oscillation Frequency: 10 to 2000 to 10Hz for 20 minute, 2 hours in each of 3 mutually perpendicular directions. |
| Temperature Cycling | Appearance No damaged, Cap. Change Within ±12.5%, I.R. Meet the initial rated value, DC Resistance 0.05Ωmax. | Soldered on glass-epoxy substrate, 10 cycles |
| Humidity Test | Appearance No damaged, Cap. Change Within ±12.5%, I.R. 105MΩmin. (for 473,104,224,474,105), 25MΩmin. (for 435), 5MΩmin. (for 755,915), DC Resistance 0.05Ωmax. | Soldered on glass-epoxy substrate, Temperature: 40±2°C, Humidity: 90 to 95%(RH), Time: 500+24 / -0 hours |
| Heat Life Test | Appearance No damaged, Cap. Change Within ±12.5%, I.R. 105MΩmin. (for 473,104,224,474,105), 25MΩmin. (for 435), 5MΩmin. (for 755,915), DC Resistance 0.05Ωmax. | Soldered on glass-epoxy substrate, Temperature: Maximum Operating Temperature ± 2 °C, Test Voltage: Rated Voltage x 150%, Time: 1000+48 / -0 hours |
| Packaging Unit | 10000 pcs./Reel (PAPER Tape) | |